Bradite Fastrac Anticorrosive Primer

£35.00

Fastrac Anticorrosive Primer is a fast drying modified alkyd anticorrosive primer for properly prepared ferrous surfaces.

Bradite Fastrac Anticorrosive Primer is intended for use as a general purpose fast drying modified alkyd primer, pigmented with zinc phosphate, which is suitable for general use as a system primer for steel.

This coating has good protective properties against corrosion on properly prepared steel, it will also be surface dry within an hour and can be overcoated after 16 hours of application.

It is suitable for coating over compatible coatings which are clean, dry and abraded.

This product is available in 5lt pack sizes in either a red or a grey colour.

Description

Bradite Fastrac Anticorrosive Primer is a general purpose fast drying modified alkyd primer, pigmented with zinc phosphate, which is suitable for general use as a system primer for steel.

Bradite Fastrac Anticorrosive Primer is intended for use as a general purpose fast drying prefabrication or system primer on properly prepared ferrous surfaces. It has good protective properties against corrosion and is suitable for coating over compatible coatings which are clean, dry and abraded.

This coating can be applied with either a brush, roller or either a conventional or airless spray with a minimum dry to over coat time of 16 hours. The recommended wet film thickness is 58 microns per coat which achieves a dry film thickness of 35 microns. The theoretical coverage rate by following these recommendations is 9 m² per litre. This product will be surface dry within 1 hour and will be fully cured in 7 days.

Before applying the product you should first prepare the ferrous surface by blast cleaning it to SIS Sa½ minimum or mechanically prepared to SIS St 3 minimum.

This product is available in 5lt pack sizes in either a red or a grey colour for free next day delivery throughout the UK.

Surface Preparation

Suitable for coating over compatible coatings which are clean, dry and abraded.

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Washing and rinsing should be used with scrubbing to remove grease or oil.

Remove all rust scale, loose mill scale or other corrosion products by scraping and mechanical cleaning to SIS St 3.

Ferrous Surfaces: Blast clean to SIS Sa 2½ minimum or mechanically prepared to SIS St 3 minimum.

Existing Coatings: Intact areas of coatings should be roughened by abrasive manual or disc sanding, feathering back to a sound coating edge. Cracks and pits should be filled using a suitable metal filler before painting. Substrate should be dust free and completely dry before coating.

Technical Data

Download Datasheet

Volume Solids: 60%
VOC Content:  320g/lt
Flash point:  26°C
Dry Film thickness:  35 microns
Wet Film thickness:  58 microns
Theoretical coverage:  9 m²/lt
Surface Dry:  1 hour
Full Cure: 7 days
Overcoating time 23°C:
Minimum 16 hrs